Polymeric additive for improving polymer environmental stress cracking resistance properties

ABSTRACT

A polymer composition may include a crosslinked polymeric additive composition that includes a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent; and a secondary polymer composition.

CROSS-REFERENCE TO RELATED APPLICATIONS

This Application is a continuation of PCT/IB2019/020010 filed on Apr. 19, 2019, which claims priority to U.S. Provisional Patent Application No. 62/678,816 filed on May 31, 2018, and this application is also a continuation-in-part application of U.S. patent application Ser. No. 15/282,169 filed on Sep. 30, 2016, which claims priority to U.S. Provisional Patent Application No. 62/236,042 filed on Oct. 1, 2015, all of which are incorporated herein by reference.

BACKGROUND

Polyolefins such as polyethylene (PE) and polypropylene (PP) may be used to manufacture a varied range of articles, including films, molded products, foams, and the like. Polyolefins may have characteristics such as high processability, low production cost, flexibility, low density and recycling possibility. However, physical and chemical properties of polyolefin compositions may exhibit varied responses depending on a number of factors such as molecular weight, distribution of molecular weights, content and distribution of comonomer (or comonomers), method of processing, and the like.

Methods of manufacturing may utilize polyolefin's limited inter- and intra-molecular interactions, capitalizing on the high degree of freedom in the polymer to form different microstructures, and to modify the polymer to provide varied uses in a number of technical markets. However, polyolefin materials may have a number of limitations, which can restrict application such as susceptibility to deformation and degradation in the presence of some chemical agents, and low barrier properties to various gases and a number of volatile organic compounds (VOC). Property limitations may hinder the use of polyolefin materials in the production of articles requiring low permeability to gases and solvents, such as packaging for food products, chemicals, household chemicals, agrochemicals, fuel tanks, water and gas pipes, and geomembranes, for example.

While polyolefins are utilized in industrial applications because of favorable characteristics such as high processability, low production cost, flexibility, low density, and ease of recycling, polyolefin compositions may have physical limitations, such as susceptibility to environmental stress cracking (ESC) and accelerated slow crack growth (SCG), which may occur below the yield strength limit of the material when subjected to long-term mechanical stress. Polyolefin materials may also exhibit sensitivity to certain groups of chemical substances, which can lead to deformation and degradation. As a result, chemical sensitivities and physical limitations may limit the success in the replacement of other industry standard materials, such as steel and glass, with polyolefin materials because the material durability is insufficient to prevent chemical damage and spillage.

Conventionally, methods of altering the chemical nature of the polymer composition may include modifying the polymer synthesis technique or the inclusion of one or more comonomers. However, modifying the polyolefin may also result in undesirable side effects. By way of illustration, increasing the molecular weight of a polyolefin may produce changes in the SCG and ESC, but can also increase viscosity, which may limit the processability and moldability of the polymer composition.

Other strategies may include inclusion of a comonomer and/or blending polyolefins with other polymer classes and additives to confer various physical and chemical attributes. For example, polyolefins may be copolymerized with alpha-olefins having a lower elastic modulus, which results in a considerable increase in environmental stress cracking resistance (ESCR) and resistance to impact but adversely affects the stiffness of the polymer. However, the use of alpha-olefins may have limited effectiveness because, while the incorporation of alpha-olefin comonomers must occur in the high molecular weight fraction in order to affect ESC and impact resistance, many popular catalyst systems have a low probability of inserting alpha-olefins in the high molecular weight fraction, an important factor in forming “tie molecules” between the chains of the surrounding polyolefin that are responsible for transferring stress between the crystalline regions and, consequently, responsible for important mechanical properties. The result is the production of a polymer composition having reduced structural stiffness. It is also noted that, while advances have developed catalysts that increase the likelihood of displacing the incorporation of a comonomer to the highest molecular weight range, and that multiple reactors may be used to address these limitations, such modifications are expensive alternatives and not wholly effective in balancing resistance to impact and ESC without negatively affecting stiffness.

Polymer modification by blending may vary the chemical nature of the composition, resulting in changes to the overall physical properties of the material. Material changes introduced by polymer blending may be unpredictable, however, and, depending on the nature of the polymers and additives incorporated, the resulting changes may be uneven and some material attributes may be enhanced while others exhibit notable deficits. The incorporation of a second phase into the matrix polymer, which generally has a different chemical nature, may increase the resistance to impact and ESC resistance in some cases. However, like the copolymerization strategy, polymer blends are often accompanied by a marked loss in stiffness, because the blended materials may have lower elastic modulus than the matrix polyolefin.

Accordingly, a continuing need exists for developments in polyolefin compositions to have increases in environmental stress cracking resistance while balancing the mechanical properties of the polymer.

SUMMARY

This summary introduces a selection of concepts that are described below in more detail. This summary is not intended to identify key or essential features of the claimed subject matter, nor is it intended to be used as an aid in limiting the scope of the claimed subject matter.

In one aspect, embodiments disclosed herein relate to a polymer composition that includes a crosslinked polymeric additive composition that includes a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent; and a secondary polymer composition.

In another aspect, embodiments disclosed herein relate to a manufactured article that includes a polymer composition that includes a crosslinked polymeric additive composition that includes a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent; and a secondary polymer composition.

In yet another aspect, embodiments disclosed herein relate to a method that includes combining a crosslinked polymeric additive composition with a secondary polymer composition; wherein the crosslinked polymeric additive composition comprises a matrix polymer having a polar polymer internal phase that is selectively crosslinked with a crosslinking agent; and wherein combining the crosslinked polymeric additive composition with the secondary polymer compositions improves the environmental stress cracking resistance of the polymer composition with respect to the secondary polymer composition alone.

In yet another aspect, embodiments disclosed herein relate to a use of a crosslinked polymeric additive composition to improve the properties of a secondary polymer composition, the crosslinked polymeric additive composition comprising a matrix polymer having a polar polymer internal phase that is selectively crosslinked with a crosslinking agent.

Other aspects and advantages of the claimed subject matter will be apparent from the following description and the appended claims.

DETAILED DESCRIPTION

Embodiments of the present disclosure are directed to polymer compositions that contained a crosslinked polymeric additive composition that may be used to improve the properties (including but not limited to environmental stress cracking resistance) of a secondary polymer composition. The crosslinked polymeric additive composition may include a matrix polymer of a polyolefin and one or more polymer particles dispersed in the polymer matrix, where one or more polymer particles includes a polar polymer that is selectively crosslinked with a crosslinking agent. In particular, the crosslinked polymeric additive composition may provide function to improve the properties of the secondary polymer composition to which the crosslinked polymeric additive composition is added. The crosslinked polymer additive composition containing a mixture of polyolefin and polar polymer particles that may induce structural and/or morphological changes when compared to an unmodified polymer or blend, which may provide for the property improvement in the secondary polymer composition.

For example, polymer compositions in accordance with the present disclosure may exhibit improvements in environmental stress cracking resistance, while also maintaining a balance of mechanical properties. In one or more embodiments, polymer compositions may be blended with a crosslinked polymeric additive to adjust various physical and chemical properties of the final composition. Specifically, in one or more embodiments, physical and chemical properties of a polymer or polymer blend may be modified blending with a crosslinked polymeric additive incorporating a crosslinked polar polymer internal phase. In some embodiments, crosslinked polymer additives may also contain a functionalized polyolefin that may be added as a compatibilizing agent, in addition to other additives. Processes of manufacturing polymer compositions in accordance with the present disclosure may include various blending methods such a solution, emulsion, suspension, or extrusion.

Crosslinked polymeric additives in accordance with the present disclosure may be formulated as a “masterbatch” in which the polymer composition contains concentrations of polar polymer that are high relative to the polar polymer concentration in a final polymer blend for manufacture or use. For example, a masterbatch stock may be formulated for storage or transport and, when desired, be combined with additional polyolefin or other materials in order to produce a final polymer composition having concentration of constituent components that provides physical and chemical properties tailored to a selected end-use.

In some embodiments, the polar polymer within the polymer composition may be crosslinked by a crosslinking agent to generate particulates containing intra-particle covalent linkages between the constituent polar polymer chains. Depending on the concentration and relative proximity of adjacent polar polymer particles, inter-particle covalent linkages may also be formed. The crosslinked polar polymer particles may create changes in the physical and physicochemical properties, including increases in ESCR and improvement in the balance of stiffness/impact resistance mechanical properties in relation to the properties of pure (unmodified or blended) polyolefins, as well as to secondary polymer compositions to which the crosslinked polymeric additive was added.

In one or more embodiments, the balance of properties for modified polymer compositions may be expressed through a property balance index, which considers the combination of the flexural modulus, impact resistance and ESCR, discussed in more detail below. The property balance index may be normalized against a reference polyolefin (without the polar polymer, etc.), and advantageously, the polymer compositions of the present disclosure may achieve a normalized property balance index that ranges from about 1.5 to 10, or greater than 1.5, or greater than 1.8, or from 3 to 6 in more particular embodiments.

Crosslinked Polymeric Additive

In one or more embodiments, polymer additives in accordance with the present disclosure may include a polymeric additive that may contain a polyolefin matrix polymer having an internal polar polymer phase that is crosslinked by a suitable crosslinking agent. Crosslinked polymeric additives may be blended with various polymer types to modify a number of properties including stress cracking resistance, and the like.

Matrix Polymer

Crosslinked polymeric additives in accordance with the present disclosure may include a matrix polymer component that surrounds other components in the composition, including polar polymer particles and other additives. In one or more embodiments, matrix polymers may include polyolefins produced from unsaturated monomers with the general chemical formula of C_(n)H_(2n). In some embodiments, polyolefins may include ethylene homopolymers, copolymers of ethylene and one or more C3-C20 alpha-olefins, propylene homopolymers, heterophasic propylene polymers, copolymers of propylene and one or more comonomers selected from ethylene and C4-C20 alpha-olefins, olefin terpolymers and higher order polymers, and blends obtained from the mixture of one or more of these polymers and/or copolymers.

In one or more embodiments, matrix polymer may be selected from polyethylene with a density ranging from a lower limit selected from one of 0.890, 0.900, 0.910, 0.920, 0.930 and 0.940 g/cm³ to an upper limit selected from one of 0.945, 0.950, 0.960 and 0.970 g/cm³ measured according to ASTM D792, where any lower limit can be used with any upper limit; a melt index (I₂) ranging from a lower limit selected from one of 0.01, 0.1, 1, 10 and 50 g/10 min to an upper limit selected from one of 10, 20, 50, 60, 100 and 200 g/10 min according to ASTM D1238 at 190° C./2.16 kg, where any lower limit can be used with any upper limit; and/or a melt index (I₂₁) ranging from a lower limit selected from one of 0.1, 1, 3, 5, 10 and 50 g/10 min to an upper limit selected from one of 10, 20, 30, 50, 100, 500, and 1000 g/10 min according to ASTM D1238 at 190° C./21.6 kg, where any lower limit can be used with any upper limit.

In one or more embodiments, the matrix polymer may include a high density polyethylene, with a density ranging from 0.930 g/cm³ to 0.970 g/cm³ according to ASTM D792 and a High Load Melt Index (HLMI) ranging from 1 to 60 g/10 min according to ASTM D1238 at 190° C./21.6 kg.

In one or more embodiments, polymer compositions may contain a percent by weight of the total composition (wt %) of matrix polymer ranging from a lower limit selected from one of 30 wt %, 40 wt %, 50 wt %, 60 wt %, 75 wt %, and 85 wt %, to an upper limit selected from one of 60 wt %, 75 wt %, 80 wt %, 90 wt %, 95 wt %, 99.5 wt % and 99.9 wt %, where any lower limit can be used with any upper limit.

Polar Polymers

Polymer compositions in accordance with the present disclosure may include one or more polar polymers that are combined with a polyolefin and, further, may be crosslinked by one or more crosslinking agents. As used herein, a “polar polymer” is understood to mean any polymer containing hydroxyl, carboxylic acid, carboxylate, ester, ether, acetate, amide, amine, epoxy, imide, imine, sulfone, phosphone, and their derivatives, as functional groups, among others. The polar polymer may be selectively crosslinked by an appropriate crosslinking agent, where the selective crosslinking may occur between the functional groups by reacting with a suitable crosslinking agent in the presence of polyolefins, additives, and other materials. Thus, the crosslinking agent is selected to react with the polar polymer but without exhibiting reactivity (or having minimal reactivity towards) the polyolefin. In some embodiments, polar polymers include polyvinyl alcohol (PVOH), ethylene vinyl alcohol (EVOH) copolymer, ethylene vinyl acetate copolymer (EVA) and mixtures thereof. In particular embodiments, polar polymers include polyvinyl alcohol.

One or more polar polymers in accordance with the present disclosure may be produced by hydrolyzing a polyvinyl ester to produce free hydroxyl groups on the polymer backbone. By way of example, polar polymers produced through hydrolysis may include polyvinyl alcohol generated from the hydrolysis of polyvinyl acetate. The degree of hydrolysis for a polymer hydrolyzed to produce a polar polymer may be within the range of 30% and 100% in some embodiments, and between 70% and 99% in some embodiments.

Polar polymers in accordance with the present disclosure may have an intrinsic viscosity in the range of 2 mPa·s to 110 mPa·s in some embodiments, and between 4 mPa·s and 31 mPa·s in some embodiments. Intrinsic viscosity may be measured according to DIN 53015 using a 4% aqueous solution at 20° C.

In one or more embodiments, polar polymer in accordance with the present disclosure may form a distinct phase within the polymer composition, which may be in the form of particles having an average particle size of less than 200 μm. Particle size determinations may be made in some embodiments using SEM techniques after combination of polar polymer with the polyolefin by calculating relevant statistical data regarding particle size. In some embodiments, SEM imaging may be used to calculate particle size and develop size ranges using statistical analysis known for polymers and blends. Samples may be examined using SEM after hot pressing samples in accordance with ASTM D-4703 and polishing the internal part of the plate by cryo-ultramicrotomy. Samples may be dried and submitted to metallization with gold and imaged by FESEM (Field Emission Scanning Electron Microscopy, Model Inspect F50, from FEI), or by Tabletop SEM (Model TM-1000, from Hitachi). The size of each crosslinked polar polymer particle may be measured from these images using the software such as LAS (version 43, from Leica). Calibration may be performed using the scale bar of each image and the measured values can be statistically analyzed by the software. The average value and standard deviation are given by the measurement of, at least, 300 particles.

Polar polymer particles in accordance with the present disclosure may have an average particle size having a lower limit selected from 0.01 μm, 0.5 μm, 1 μm, and 5 μm, and an upper limit selected from 10 μm, 20 μm, 30 μm, 50 μm, and 200 μm, where any lower limit may be used with any upper limit.

In one or more embodiments, polymer compositions may contain a percent by weight of the total composition (wt %) of polar polymer ranging from a lower limit selected from one of 0.1 wt %, 0.25 wt %, 0.5 wt %, 1 wt %, 2 wt %, 5 wt %, 10 wt %, 15 wt %, and 25 wt %, to an upper limit selected from one of 5 wt %, 10 wt %, 15 wt %, 25 wt %, 50 wt %, 60 wt %, and 70 wt %, where any lower limit can be used with any upper limit.

Functionalized Polyolefin

In some embodiments, compatibilizing agents such as functionalized polyolefins may be optionally added to modify the interactions between the polyolefin and the polar polymer. As used herein, “functionalized polyolefin” (or compatibilizing agent) is understood to mean any polyolefin which had its chemical composition altered by grafting or copolymerization, or other chemical process, using polar functionalizing reagents. Functionalized polyolefins in accordance with the present disclosure include polyolefins functionalized with maleic anhydride, maleic acid, acrylic acid, methacrylic acid, itaconic acid, itaconic anhydride, methacrylate, acrylate, epoxy, silane, succinic acid, succinic anhydride, ionomers, and their derivatives, or any other polar comonomer, and mixtures thereof, produced in a reactor or by grafting.

In one or more embodiments, polymer compositions may contain a percent by weight of the total composition (wt %) of functionalized polyolefin ranging from a lower limit selected from one of 0.1 wt %, 0.5 wt %, 1 wt %, and 5 wt %, to an upper limit selected from one of 5 wt %, 7.5 wt %, 10 wt %, and 15 wt %, where any lower limit can be used with any upper limit.

Crosslinking Agent

In one or more embodiments, a crosslinking agent may be used to crosslink a selected polymer phase in a polymer composition. As used herein, a “crosslinking agent” is understood to mean any bi- or multi-functional chemical substance capable of reacting selectively with the polar groups of a polymer, forming crosslinks between and within the constituent polymer chains. As used herein, “selective” or “selectively” used alone or in conjunction with “crosslinking” or “crosslinked” is used to specify that the crosslinking agent reacts exclusively with the polar polymer, or that the crosslinking agent reacts with the polar polymer to a substantially greater degree (98% or greater, for example) than with respect to the polyolefin polymer.

Crosslinking agents in accordance with the present disclosure may react preferentially with a polar polymer, and may be non-reactive (or substantially non-reactive) with polyolefin. The crosslinking agent is considered non-reactive (or not substantially reactive) to polyolefin when a composition consisting of the crosslinking agent and polyolefin may be processed with no changes or variations within a value of 2% (or lower) in rheology (complex viscosity), FTIR, and ESCR according to any applicable measurement method, as compared to a composition containing the polyolefin alone, according to any applicable measurement method provided the same method is applied to the comparative polyolefin and to the composition consisting of polyolefin and crosslinking agent.

In one or more embodiments, crosslinking agents in accordance with the present disclosure may include linear, branched, saturated, and unsaturated carbon chains containing functional groups that react with counterpart functional groups present on the backbone and termini of a polar polymer incorporated into a polymer composition. In some embodiments, crosslinking agents may be added to a pre-mixed polymer blend containing a polyolefin and polar polymer particles, in order to crosslink the polar polymer in the presence of the polyolefin. Following addition to the pre-mixed polymer blend, a crosslinking agent may react with the polar polymer within the particles, creating intraparticle crosslinks between the polar polymer chains. Crosslinking agents in accordance with the present disclosure may include, for example, maleic anhydride, maleic acid, itaconic acid, itaconic anhydride, succinic acid, succinic anhydride, succinic aldehyde, adipic acid, adipic anhydride, phthalic anhydride, pthalic acid, citric acid, glutaconic acid, glutaconic anhydride, glutaraldehyde, sodium tetraborate, organic titanates such as tetrabutyl titanate, organic zirconates such as zirconium(IV) bis(diethyl citrato)dipropoxide, methoxy polyethylene glycol acrylates, ethoxy polyethylene glycol acrylates, ethylene glycol diacrylate, ethylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, 1,3-butylene glycol dimethacrylate, neopentyl glycol diacrylate, neopentyl glycol dimethacrylate, trimethylol ethane triacrylate, trimethylol ethane trimethacrylate, trimethylol propane triacrylate, trimethylol propane trimethacrylate, and tetramethylol methane tetracrylate, their derivatives and mixtures thereof.

In one or more embodiments, crosslinking agents may be added to a blend used to form a polymer composition, such as the crosslinked polymeric additive, at a percent by weight (wt %) of the blend ranging from a lower limit selected from one of 0.001 wt %, 0.01 wt %, 0.05 wt %, 0.5 wt %, 1 wt %, and 2 wt % to an upper limit selected from one of 1.5 wt %, 2 wt %, 5 wt %, and 10 wt %, where any lower limit can be used with any upper limit.

Secondary Polymer Compositions

Polymer compositions in accordance with the present disclosure may include a mixture of crosslinked polymeric additive with a secondary polymer composition. While a number of exemplary polymer materials are described below it is envisioned that the secondary polymer composition may be any polymer suited for manufacturing applications.

In one or more embodiments, the secondary polymer compositions may be selected from polyolefin, polystyrene, polyamide, polyester, ethylene vinyl alcohol, polyacrylate, polymethacrylate, poly(vinyl chloride), polycarbonate, polyssacharides, and rubber. Specifically, in one or more embodiments, the secondary polymer compositions may be selected from polyethylene, polypropylene, polystyrene, poly(ethylene terephthalate), poly(vinyl chloride), polycarbonate, poly(methyl methacrylate) and polyamide. Further, it is also envisioned that any of the secondary polymers may be at least partially biobased. In one or more embodiments, the secondary polymer composition (including any of the above) may be a virgin polymer resin, while in others embodiments, the secondary polymer resin is a post-industrial polymer resin (PIR), a post-consumer polymer resin (PCR), a regrind polymer resin or combinations thereof.

It is recognized that recycling of polymeric materials is a major concern for the environment. Generally. the recycling of PCR resins is difficult due to degradation of the ESCR properties of the material as compared to virgin resins, which limits possible end use applications. It was surprisingly discovered that the addition of the crosslinked polymeric additive as described in the present disclosure, even in very low concentrations, enables the increase in ESCR property of PIRs and PCRs, making reuse of recycled articles possible even in applications that require high ESCR, which is normally impossible to achieve with recycled resins. In particular embodiments, PIRs, PCRs, regrind polymer resins, and combinations thereof may be present in a polymer composition in an amount higher than about 70 wt %, 80 wt %, 90 wt %, 95 wt %, 96 wt %, 97 wt %, 98 wt % or 99 wt %.

In one or more embodiments, secondary polymer compositions may include homopolymers, copolymers, graft copolymers, and heterophasic polymers. In some embodiments, secondary polymer compositions may include acrylonitrile; butadiene-styrene (ABS); polyvinyl chloride (PVC); polyesters that include polylactic acid (PLA), polyglycolic acid (PGA), poly-co-lactic-glycolic acid (PLGA), and the like; polyamides that include various nylons; polyacrylamide, polyacrylates, polymethacrylates; polyvinylalcohol (PVOH); polyolefins such as polypropylene polymers and copolymers; high melt strength polyolefins that include branched polyolefins and crosslinked polyolefins; polyolefin copolymers such as ethylene vinyl acetate (EVA); heterophasic polyolefins; polycarbonate (PC), polystyrene (PS); high impact polystyrene (HIPS), polycaprolactone (PCL); and the like.

In one or more embodiments, secondary polymer may be selected from polyethylene with a density ranging from a lower limit selected from one of 0.890, 0.900, 0.910, 0.920, 0.930 and 0.940 g/cm³ to an upper limit selected from one of 0.945, 0.950, 0.960 and 0.970 g/cm³ measured according to ASTM D792, where any lower limit may be used in combination with any upper limit; a melt index (I₂) ranging from a lower limit selected from one of 0.01, 0.1, 1, 10 and 50 g/10 min to an upper limit selected from one of 10, 20, 50, 100, and 200 g/10 min according to ASTM D1238 at 190° C./2.16 kg, where any lower limit may be used in combination with any upper limit; and/or a melt index (I₂₁) ranging from a lower limit selected from one of 0.1, 1, 3. 5 10 and 50 g/10 min to an upper limit selected from one of 10, 20, 30, 50, 60, 100, 500, and 1000 g/10 min according to ASTM D1238 at 190° C./21.6 kg, wherein any lower limit may be used in combination with any upper limit.

In one or more embodiments, the secondary polymer may include a high density polyethylene, with a density ranging from 0.930 g/cm³ to 0.970 g/cm³ according to ASTM D792 and a High Load Melt Index (HLMI) ranging from 1 to 60 g/10 min according to ASTM D1238 at 190° C./21.6 kg.

In one or more embodiments, the secondary polymer may be present in the polymer composition in an amount ranging from 5 to 99.9 wt % of the polymer composition, including having a lower limit of 5, 10, 15, 20, 25, 30, 35, 40, 45, or 50 wt % and an upper limit of 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 99, or 99.9 wt %, where any lower limit can be used with any upper limit.

Additives

In one or more embodiments, the polymer compositions of the present disclosure may contain a number of other functional additives that modify various properties of the composition such as antioxidants, pigments, fillers, reinforcements, adhesion-promoting agents, biocides, whitening agents, nucleating agents, anti-statics, anti-blocking agents, processing aids, flame-retardants, plasticizers, light stabilizers, and the like.

Polymer compositions in accordance with the present disclosure may include fillers and additives that modify various physical and chemical properties when added to the polymer composition during blending. In one or more embodiments, fillers and nanofillers may be added to a polymer composition to increase the barrier properties of the material by increasing the tortuous path of the polymer matrix for the passage of permeate molecules. As used herein, “nanofiller” is defined as any inorganic substance with at least a nanometric scale dimension. Polymer composition in accordance with the present disclosure may be loaded with a filler and/or nanofiller that may include polyhedral oligomeric silsesquioxane (POSS), clays, nanoclays, silica particles, nanosilica, calcium nanocarbonate, metal oxide particles and nanoparticles, inorganic salt particles and nanoparticles, and mixtures thereof.

In one or more embodiments, fillers and/or nanofillers in accordance with the present disclosure may be incorporated into a polymer composition at a percent by weight (wt %) up to 70 wt %.

In one or more embodiments, polymer compositions may contain a percent by weight of the total composition (wt %) of one or more additives ranging from a lower limit selected from one of 0.001 wt %, 0.01 wt %, 0.05 wt %, 0.5 wt %, and 1 wt %, to an upper limit selected from one of 1.5 wt %, 2 wt %, 5 wt %, and 7 wt %, where any lower limit can be used with any upper limit.

Masterbatch Formulations

One or more of the wt % values mentioned above with respect to each of the components refer in fact to amounts that may be used to form such a masterbatch. In one or more embodiments, a masterbatch polymer composition may contain a percent by weight of the total composition (wt %) of crosslinked polar polymer ranging from a lower limit selected from one of 10 wt %, 20 wt % 25 wt %, 30 wt %, 40 wt %, and 50 wt % to an upper limit selected from one of 50 wt %, 60 wt %, and 70 wt %, where any lower limit can be used with any upper limit. In particular, as discussed herein, the crosslinked polymeric additive composition may be formulated as a masterbatch formulation that is combined with a secondary polymer composition to improve the properties of the secondary polymer composition, which may be a virgin polymer resin or a recycled material (including post-industrial resins, post-consumer resins, and regrind polymer resin). Specifically, even for overly degraded recycled materials, the masterbatch formulation (crosslinked polymeric additive composition) may be used to improve the properties of the secondary polymer composition in order to recover or restore (at least partially or wholly) the properties of the secondary polymer composition to its original level (i.e., to a level that is close to or substantially the same as a virgin resin thereof) or higher than the original level.

As noted, in the masterbatch composition, the polymer composition contains concentrations of polar polymer that are high relative to the polar polymer concentration in a final polymer blend for manufacture or use. Thus, prior to use to form a manufactured article, the masterbatch composition may be combined with an additional quantity of secondary polymer to arrive at a polar polymer concentration in the final composition that is lower than the masterbatch concentration. For example, the crosslinked polymeric additive composition may be present in the final polymer composition (combined with the secondary polymer composition) at a percent by weight of the polymer composition that ranges from 0.01 wt % to 95 wt %, where the lower limit may include any of 0.01, 1, 5, 10, 15, 20, 25, 30, 35, 40, 45, or 50 wt %, and the upper limit includes any of 50, 55, 60, 65, 70 75, 80, 85, 90, or 95 wt %, where any lower limit can be used in combination with any upper limit.

Polymer Composition Preparation Methods

Polymer compositions in accordance with the present disclosure may be prepared by a number of possible polymer blending and formulation techniques, which will be discussed in the following sections. In particular, as described herein, a crosslinked polymeric additive composition may be combined with a secondary polymer composition; wherein combining the crosslinked polymeric additive composition with the secondary polymer compositions improves the environmental stress cracking resistance of the polymer composition with respect to the secondary polymer composition alone.

In one or more embodiments, the crosslinked polymeric additive composition is combined with a secondary polymer composition in a melt blend process. In one or more other embodiments, the crosslinked polymeric additive composition is combined with a secondary polymer composition in a dry blend process. Thus, the crosslinked polymeric additive may be formulated as a masterbatch formulation that may be diluted in a subsequent melt-blend or dry blend process to form the final polymer composition having the improved properties. For example, the crosslinked polymeric additive composition may be initially formed, such as in a reactive extrusion process or the like to form the selectively crosslinked polymer particles within the matrix polymer. Such crosslinked polymeric additive composition may subsequently be combined with a secondary polymer composition, may be subjected to a conventional extrusion process (melt-blending), for example, to blend the polymers together, thereby forming an improved secondary polymer or it may be mixed manually or in a dry-mixer or even added directly together with the secondary polymer (dry-blending) into the hopper of the plastic manufacturing machine, such as a blowmolding or a injection molding machine.

Extrusion

In one or more embodiments, crosslinked polymeric additive compositions in accordance with the present disclosure may be prepared using continuous or discontinuous extrusion. Methods may use single-, twin- or multi-screw extruders, which may be used at temperatures ranging from 100° C. to 270° C. in some embodiments, and from 140° C. to 230° C. in some embodiments. In some embodiments, raw materials are added to an extruder, simultaneously or sequentially, into the main or secondary feeders in the form of powder, granules, flakes or dispersion in liquids as solutions, emulsions and suspensions of one or more components.

The components can be pre-dispersed in prior processes using intensive mixers, for example. Inside an extrusion equipment, the components are heated by heat exchange and/or mechanical friction, the phases are melt and the dispersion occurs by the deformation of the polymer. In some embodiments, one or more compatibilizing agents (such as a functionalized polyolefin) between polymers of different natures may be used to facilitate and/or refine the distribution of the polymer phases and to enable the formation of the morphology of conventional blend and/or particles. The crosslinking agent can be added at the same extrusion stage or in a consecutive extrusion, according to selectivity and reactivity of the system.

In one or more embodiments, methods of preparing polymer compositions may involve a single extrusion or multiple extrusions following the sequences of the blend preparation stages. Blending and extrusion also involve the selective crosslinking of the polar polymer in the dispersed phase of the polymer composition by the crosslinking agent.

Extrusion techniques in accordance with the present disclosure may also involve the preparation of a polar polymer concentrate (a masterbatch), combined with a crosslinking agent in some embodiments, that is then combined with other components to produce a polymer composition of the present disclosure. In some embodiments, the morphology of a crosslinked polar polymer may be stabilized by crosslinking when dispersed in a polymer matrix containing polyolefins and is not dependent on subsequent processes for defining the morphology.

Polymer compositions prepared by melt-blending or dry-blending may be in the form of granules that are applicable to different molding processes, including processes selected from extrusion molding, injection molding, thermoforming, cast film extrusion, blown film extrusion, foaming, extrusion blow-molding, ISBM (Injection Stretched Blow-Molding), rotomolding, pultrusion, additive manufacturing, lamination, and the like, to produce manufactured articles. Specifically, in one or more embodiments, the article is an injection molded article, a thermoformed article, a film, a foam, a blow molded article, a 3D printed article, a compressed article, a coextruded article, a laminated article, an injection blow molded article, a rotomolded article, an extruded article, or a pultruded article.

Applications

In one or more embodiments, polymer compositions may be used in the manufacturing of articles, including rigid and flexible packaging for food products, household chemicals, chemicals, agrochemicals, fuel tanks, water and gas pipes, geomembranes, recycled articles, and the like.

EXAMPLES

In the following examples, a number of polymer samples are analyzed to demonstrate the changes in physical and chemical properties associated with polymer compositions prepared in accordance with the present disclosure.

Characterization Techniques

Prepared samples were characterized using a number of standardized and lab-based polymer characterization techniques discussed below.

Environmental Stress Cracking Resistance (ESCR)

For environmental stress cracking resistance tests, sample formulations were compression molded in 2 mm thick plaques according to ASTM D-4703, at 200° C. and under pressure. Samples were notched, bent to achieve deformation and placed in a metal U-shaped specimen holder, and placed in an aqueous solution containing nonylphenol ethoxylate (IGEPAL™ CO-630 from Solvay) at a percent by volume (vol %) of 10 vol %. Failure was determined as the appearance of any crack visible by the naked eye, in accordance with ASTM D-1693 procedure B.

Flexural Modulus

The flexural modulus of the material given by the secant modulus at 1% of deformation was determined in the flexural resistance test in accordance with ASTM D-790. The samples were previously compression molded in plaques in accordance with ASTM D4703.

IZOD Impact Resistance Test

The IZOD impact resistance at 23° C. of the material was determined according to ASTM D-256. Samples were previously compression molded in plaques in accordance with ASTM D4703.

Definition of the Property Balance Index

Changes in physical and chemical properties of polymer compositions in accordance with the present disclosure are characterized using an index of properties that may be used to quantify the changes in a respective polymer composition based on a balance of mechanical and ESCR properties. Improvements in a material's flexural modulus, impact resistance and ESCR may translate to better performance in various applications. However, improvements in a single property may be offset by losses in other properties. In order to quantify the overall improvement of the material, the product of the individual properties is monitored in the examples below. The “Property Balance Index” (PBI) is defined as shown in Eq. 1 to quantify the property changes, wherein “FM” is the flexural modulus given by the secant modulus at 1% of deformation measured according to ASTM D-790 in MPa, “IR” is the IZOD impact resistance at 23° C. measured according to ASTM D-256 in Jim and “ESCR” is the environmental stress cracking resistance measured according to ASTM D-1693 procedure B in hours (h).

$\begin{matrix} {{P\; B\; I} = \frac{{FM} \times {IR} \times {ESCR}}{10^{7}}} & (1) \end{matrix}$

Definition of the Normalized Property Balance Index

To compare the magnitude of property changes for different polymer systems, the PBI values were normalized according to Eq. 2, where N_(PBI) is the normalized property balance index, PBI_(sample) is the property balance index obtained for the samples of polymer composition including the crosslinked polymeric additive and the secondary polymer and PBI_(reference) is the property balance index obtained for the reference samples, i.e., a polymer composition comprising the secondary polymer without the crosslinked polymeric additive.

$\begin{matrix} {N_{PBI} = \frac{P\; B\; I_{sample}}{P\; B\; I_{reference}}} & (2) \end{matrix}$

Polymer compositions in accordance with the present disclosure may exhibit an N_(PBI) higher than about 1.0 or higher than about one of 1.5, 2.0, 3.0, 5.0 and 10. In another embodiment, polymer compositions in accordance with the present disclosure may exhibit an N_(PBI) falling within the range of 1.5 to 10 in some embodiments, and within the range of 3 to 9 in some embodiments. Polymer compositions in accordance with the present disclosure may exhibit an NPBI that is at least 1.5 in other embodiments. In some embodiments, the N_(PBI) value is greater than 1.8.

A crosslinked polymeric additive was formulated as a masterbatch composition, containing 50 wt % of polyethylene as a matrix polymer and 50 wt % of selectively crosslinked PVOH based in the masterbatch composition, which was combined with high density polyethylene (HDPE) to final contents of 3, 4 and 5 wt % of selectively crosslinked PVOH and processed in ZSK26 twin screw extruder or extrusion blow molding equipment. Trials with different polyethylene (PE) resin were performed to observe the final product properties. Four different methods of combination with the HDPE resin were used. The additives used are primary and secondary antioxidants commonly used for HDPE resins.

Method A: Neat HDPE with antioxidants additivation in extrusion, named as additivated HDPE (extrusion—ZSK26 twin screw)

Method B: Melt-blend of the crosslinked polymer additive masterbatch with neat HDPE and antioxidants additives in extrusion (extrusion—ZSK26 twin screw)

Method C: Melt-blend of the masterbatch of the crosslinked polymer additive with additivated HDPE (prepared by Method A) (extrusion—ZSK26 twin screw)

Method D: Blow-molding of additivated HDPE (prepared by Method A) without masterbatch.

Method E: Blow molding of dry-blend of masterbatch with additivated HDPE (prepared by Method A) in the blow-molding machine's hopper and posterior blow-molding

The resins used in combination (secondary polymer composition) with the masterbatch composition (to improve the properties of the resins) include those shown in Table 1 below:

TABLE 1 Modality of High Load molecular Melt Melt Commercial weight Index Index resin (from Co- distribution (190° C. @ (190° C. @ Density Resin Braskem) Catalyst monomer* (MWD) 2.16 kg) 21.6 kg) (g/cm³) 1 HS5608 Chromium 1-hexene Monomodal — 8.5 0.955 2 GF4950HS Ziegler 1-Butene Bimodal 0.21 20 0.951 natta 3 GF4950 Ziegler 1-Butene Bimodal 0.36 28 0.956 natta 4 GF4960 Ziegler — Bimodal 0.34 28 0.961 natta *The content of co-monomers is generally <1%.

As shown in Table 2 that the combination of HDPE and masterbatch show an increase in ESCR results and N_(PBI) values if compared to additivated samples HDPE (produced by method A).

TABLE 2 ESCR (h) (ASTM D-1693 Sample Method procedure B) N_(PBI) Resin 1 A 258 1.00 D 165 0.58 Resin 1 with 3 wt % B 111 2.62 of crosslinked PVOH C 549 1.82 E 516 2.15 Resin 1 with 4 wt % B >1000 4.91 of crosslinked PVOH C >1000 3.63 E 713 3.03 Resin 1 with 5 wt % B >1000 3.87 of crosslinked PVOH C >1000 3.47 E >1000 4.83 Resin 2 A 130 1 D 100 0.72 Resin 2 with 3 wt % B 451 3.28 of crosslinked PVOH C 747 5.81 E 349 2.91 Resin 2 with 4 wt % B 506 3.62 of crosslinked PVOH C >1000 7.48* E 787 6.52 Resin 2 with 5 wt % B >1000 7.64* of crosslinked PVOH C >1000 7.86* E >1000 8.06* Resin 3 A 32 1 D 41 1.34 Resin 3 with 3 wt % B 105 3.46 of crosslinked PVOH C 96 3.36 E 121 3.90 Resin 3 with 4 wt % B 161 5.15 of crosslinked PVOH C 145 4.47 E 141 4.69 Resin 3 with 5 wt % B 177 5.45 of crosslinked PVOH C 198 6.37 E 160 5.02 Resin 4 A 13 1 D 14 1.39 Resin 4 with 3 wt % B 34 3.52 of crosslinked PVOH C 34 3.22 E 18 1.74 Resin 4 with 4 wt % B 37 3.78 of crosslinked PVOH C 25 2.40 E 21 2.20 Resin 4 with 5 wt % B 33 3.14 of crosslinked PVOH C 38 3.50 E 28 2.62 *For samples that the ESCR values were greater than 1000 h, the N_(PBI) was calculated considering the value of ESCR as 1000 h.

Regardless of the method used, Resin 1, Resin 2, and Resin 3 showed increase in ESCR results and NPBI (Table 2) according to the raising in the concentration of crosslinked PVOH (and consequently in the added masterbatch) (3%→5%) added in HDPE resin.

Regarding the kind of method used to add the masterbatch in HDPE, there was a little variation in N_(PBI) values in the samples produced. However, the amount of crosslinked PVOH in the samples show a change in the properties (mainly ESCR and N_(PBI) values).

According to the results showed in Table 3 and Table 4, it can be observed that there are not significant changes in the some physical chemical and mechanical properties of HDPE modified with 3, 4 and 5 wt % of crosslinked PVOH or due to the method used to obtain the samples.

TABLE 3 Tensile Impact Strength Flexural IZOD impact (kJ/m²) Yield Rupture Modulus resistance Charpy (ASTM D- Stress Stress Yield Strain (MPa) at 23° C. Impact 40° C. 1822) “S” (MPa) (MPa) (%) Rupture Strain (ASTM D- (J/m) (J/m) type (ASTM (ASTM (ASTM D- (%) Sample Method 790) (ASTM D-256) (ISO-179) specimen D-638) D-638) 638) (ASTM D-638) Resin 1 A 1196  280.8 ± 14.5  98.2 ± 22.1 233 ± 60 27.7 ± 0.4 36.9 ± 1.9 9.2 ± 0.3 1645 ± 80.0  D 1098 ± 13  276.2 ± 23.9  95.7 ± 22.5 246 ± 28 28.2 ± 0.4 30.4 ± 1.2 9.3 ± 0.3 1384 ± 40.1  Resin 1 with 3 wt % B 1229  255.4 ± 40.5  144.1 ± 198.6 165 ± 27 28.2 ± 0.5 24.3 ± 1.6 8.7 ± 0.1 1110 ± 49.4  of crosslinked PVOH C 1164 ± 10  246.5 ± 17.3 77.0 ± 3.6 161 ± 17 28.0 ± 0.4 24.0 ± 4.2 9.3 ± 0.4 995 ± 278.1 E 1226 ± 10  294.4 ± 19.2 80.8 ± 2.6 171 ± 22 28.4 ± 0.8 26.3 ± 3.6 8.8 ± 0.3 1183 ± 105.9  Resin 1 with 4 wt % B 1240  343.0 ± 32.6 80.1 ± 4   159 ± 12 28.0 ± 0.2 24.9 ± 2.5 8.9 ± 0.1 1162 ± 101.9  of crosslinked PVOH C 1221 ± 17  257.4 ± 17.4 75.4 ± 2.8 173 ± 44 28.3 ± 0.4 23.7 ± 4.4 9.0 ± 0.1 985 ± 310.2 E 1220 ± 20   302 ± 25.4 78.7 ± 2.1 169 ± 9  28.4 ± 0.4 28.1 ± 2.0 9.1 ± 0.3 1213 ± 70.3  Resin 1 with 5 wt % B 1230  272.3 ± 32.7 79.2 ± 2.3 148 ± 15 28.5 ± 0.4 26.5 ± 2.8 8.7 ± 0.1 1195 ± 106.5  of crosslinked PVOH C 1164 ± 18  258.5 ± 22.2 77.9 ± 2.1 86 ± 7 28.3 ± 0.8 24.7 ± 1.5 8.8 ± 0.3 1086 ± 85.3  E 1198 ± 27  349.1 ± 54.2 80.2 ± 3.7 160 ± 17 28.6 ± 0.5 26.8 ± 2.8 8.6 ± 0.2 1178 ± 106.2  Resin 2 A 1048 155.5 ± 4.9 76.4 ± 5.7 214 ± 18 26.2 ± 0.6 36.1 ± 2.3 9.3 ± 0.2 1722 ± 109.5  D 1024 ± 12 148.3 ± 5.0 74.8 ± 3.1 207 ± 36 25.6 ± 0.1 26.1 ± 5.1 9.3 ± 0.2 1358 ± 232.2  Resin 2 with 3 wt % B 1085  141.8 ± 10.9 73.1 ± 2.2 137 ± 17 26.7 ± 0.4 24.4 ± 2.2 8.9 ± 0.1 1175 ± 109.1  of crosslinked PVOH C 1118 ± 10 147.5 ± 6.4 72.2 ± 0.6 123 ± 12 26.5 ± 1.0 22.4 ± 4.8 9.1 ± 0.2 1110 ± 293.4  E 1100 ± 33 160.5 ± 8.4 78.1 ± 3.9  408 ± 617 25.9 ± 0.7 23.9 ± 5.6 8.8 ± 0.4 1130 ± 305.1  Resin 2 with 4 wt % B 1095 138.4 ± 8.2 74.5 ± 2.4 117 ± 11 26.9 ± 0.6 23.6 ± 4.0 8.9 ± 0.2 1046 ± 370.9  of crosslineked C 1126 ± 39 140.8 ± 5.4 72.3 ± 2.3 117 ± 15 27.2 ± 0.8 23.3 ± 3.7 8.8 ± 0.3 982 ± 381.3 PVOH E 1092 ± 7   160.8 ± 10.5 76.5 ± 3.2 141 ± 4  25.6 ± 0.3 21.8 ± 4.6 9.3 ± 0.2 875 ± 498.5 Resin 2 with 5 wt % B 1127 143.7 ± 4.3 72.4 ± 3.2 119 ± 12 26.8 ± 1.0 22.5 ± 5.1 8.6 ± 0.2 967 ± 259.2 of crosslinked PVOH C 1141 ± 5  146.0 ± 9.5 73.9 ± 1.2 141 ± 56 27.1 ± 1.8 25.7 ± 1.5 8.7 ± 0.3 1219 ± 92.9  E 1102 ± 21 154.9 ± 7.6 74.4 ± 2.6 119 ± 7  26.0 ± 0.3 20.3 ± 4.6 8.8 ± 0.2 899 ± 348.1 Resin 3 A 1150 112.0 ± 3.7 72.7 ± 1.9 170 ± 25 27.8 ± 0.4 36.2 ± 1.8 8.6 ± 0.3 1872 ± 39.3  D 1151 ± 13 116.6 ± 4.4 73.7 ± 1.7 173 ± 19 27.0 ± 0.6 22.2 ± 4.8 9.2 ± 0.3 1161 ± 295.7  Resin 3 with 3 wt % B 1216 111.6 ± 9.2 72.8 ± 2.6 105 ± 14 28.0 ± 0.5 17.9 ± 0.6 8.7 ± 0.2 433 ± 303.9 of crosslinked PVOH C 1244 ± 23 116.1 ± 7.6 72.7 ± 3.7 110 ± 11 27.6 ± 0.5 19.7 ± 2.7 8.8 ± 0.2 905 ± 362.4 E 1164 ± 25   114 ± 5.2 71.4 ± 2.5 119 ± 4  27.5 ± 0.3 22.8 ± 3.2 8.6 ± 0.2 1032 ± 459.8  Resin 3 with 4 wt % B 1196 110.2 ± 5.1 71.7 ± 1.7 106 ± 8  28.7 ± 0.3 20.8 ± 1.6 8.5 ± 0.3 1019 ± 143.9  of corsslinked PVOH C 1271 ± 24  99.9 ± 3.6 72.0 ± 1.2 102 ± 11 28.0 ± 1.3 17.7 ± 1.2 8.3 ± 0.4 836 ± 156.9 E 1212 ± 12 113.2 ± 7.1 72.5 ± 1.3 116 ± 7  27.7 ± 0.4 20.2 ± 2.3 8.9 ± 0.2 991 ± 183.1 Resin 3 with 5 wt % B 1229 103.3 ± 4.0 103.3 ± 4   98 ± 7 27.9 ± 0.1 18.5 ± 1.6 8.5 ± 0.1 686 ± 344.3 of crosslinked PVOH C 1267 ± 33 104.7 ± 5.3 70.9 ± 1.8 102 ± 13 27.8 ± 0.4 20.2 ± 2.5 7.8 ± 0.2 911 ± 310.8 E 1199 ± 13 107.8 ± 5.4 73.3 ± 1.5 160 ± 17 28.0 ± 0.4 18.9 ± 2.5 8.1 ± 0.3 594 ± 354.5 Resin 4 A 1505 111.7 ± 4.3 72.9 ± 2   120 ± 7  26.7 ± 0.4 24.4 ± 2.2 8.9 ± 0.1 1175 ± 109.1  D 1464 ± 21  148.3 ± 21.1 72.6 ± 1.2 128 ± 10 32.8 ± 0.3 22.9 ± 3.3 7.3 ± 0.2 1185 ± 371.3  Resin 4 with 3 wt % B 1573  143.8 ± 10.9 69.7 ± 3    95 ± 15 26.9 ± 0.6 23.6 ± 4.0 8.9 ± 0.2 1046 ± 370.9  of crosslinked PVOH C 1568 ± 39  132.2 ± 17.7 73.3 ± 3.5 174 ± 32 31.2 ± 0.4 18.9 ± 1.2 7.2 ± 0.1 225 ± 148.1 E 1465 ± 29  144.2 ± 18.4 72.4 ± 2.3 96 ± 6 33.1 ± 0.8 20.9 ± 0.6 7.2 ± 0.2 252 ± 112.8 Resin 4 with 4 wt % B 1566  142.7 ± 11.4 71.6 ± 2   88 ± 8 26.8 ± 1.0 22.5 ± 5.1 8.6 ± 0.2 967 ± 259.2 of crosslinked PVOH C 1535 ± 31  136.8 ± 28.8 71.2 ± 1.9 88 ± 6 31.7 ± 0.7 19.4 ± 1.0 6.9 ± 0.2 134 ± 80.9  E 1488 ± 24  154.0 ± 16.6 73.9 ± 1.9 96 ± 4 32.6 ± 0.4 20.6 ± 0.6 7.1 ± 0.1 316 ± 255.8 Resin 4 with 5 wt % B 1555 133.6 ± 9.4 71.3 ± 1.5  80 ± 11 26.7 ± 0.4 24.4 ± 2.2 8.9 ± 0.1 1175 ± 109.1  of crosslinked PVOH C 1526 ± 34 132.0 ± 8.2 72.8 ± 1.3 79 ± 6 31.2 ± 0.4 19.1 ± 0.6 7.2 ± 0.1 196 ± 170.8 E 1608 ± 26 127.4 ± 8.8 71.6 ± 2.0 99 ± 4 32.1 ± 0.5 20.5 ± 0.7 6.9 ± 0.2 324 ± 130.1

TABLE 4 Primary and Secondary antioxidants Melt Index (MI) (ASTM D1238) Irgafos ® I-168 190° C./ Irganox ® I-168 Active Degradation Sample Method 190° C./2.16 Kg 190° C./5 Kg 190° C./10 Kg 21.6 Kg I-1010 (ppm) (ppm) (ppm) Resin 1 A 0.06 0.34 1.65 9.79 644 943 534 D 0.07 0.39 1.71 10.14 566 258 763 Resin 1 with B 0.06 0.31 1.45 9.10 654 934 468 3 wt % of C 0.07 0.36 1.71 10.11 542 671 510 crosslinked E 0.07 0.37 1.64 9.81 522 280 567 PVOH Resin 1 with B 0.05 0.29 1.45 8.87 562 947 424 4 wt % of C 0.07 0.35 1.63 9.83 539 660 498 crosslinked E 0.08 0.37 1.6 9.52 521 290 573 PVOH Resin 1 with B 0.04 0.29 1.45 8.66 525 904 373 5 wt % of C 0.06 0.34 1.60 9.73 543 656 490 crosslinked E 0.07 0.36 1.58 9.43 543 303 545 PVOH Resin 2 A 0.23 0.95 3.92 21.14 278 1108 110 D 0.25 1.07 1.07 22.03 230 768 160 Resin 2 with B 0.21 0.92 3.74 21.07 285 1039 72 3 wt % of C 0 0.93 3.91 21.84 284 1076 88 crosslinked E 0.25 1.01 3.83 21.46 232 743 142 PVOH Resin 2 with B 0.22 0.93 3.75 19.67 289 1032 76 4 wt % of C 0.23 0.91 3.73 20.51 274 984 119 crosslinked E 0.24 0.93 3.77 20.78 213 729 157 PVOH Resin 2 with B 0.20 0.89 3.52 20.03 255 989 66 5 wt % of C 0.21 0.92 3.63 19.74 273 988 103 crosslinked E 0.24 0.92 3.65 19.88 212 694 130 PVOH Resin 3 A 0.30 1.30 5.11 27.54 132 343 72 D 0.35 1.44 5.34 27.30 110 152 258 Resin 3 with B 0.28 1.15 4.66 24.43 117 409 54 3 wt % of C 0.31 1.28 4.92 26.18 154 303 155 crosslinked E 0.30 1.29 4.82 25.28 104 162 194 PVOH Resin 3 with B 0.28 1.13 4.48 23.51 152 364 110 4 wt % of C 0.34 1.43 4.73 25.37 145 295 138 crosslinked E 0.31 1.25 4.70 24.20 98 143 213 PVOH Resin 3 with B 0.26 1.12 4.33 23.25 151 334 120 5 wt % of C 0.31 1.20 4.66 24.83 144 287 132 crosslinked E 0.32 1.22 4.59 23.96 100 154 263 PVOH Resin 4 A 0.34 1.49 5.92 30.19 121 307 143 D 0.38 1.62 6.03 30.75 81 74 302 Resin 4 with B 0.28 1.27 5.11 26.43 137 392 <50 3 wt % of C 0.33 1.40 5.62 29.79 122 302 144 crosslinked E 0.33 1.43 5.37 28.40 85 123 278 PVOH Resin 4 with B 0.31 1.28 5.00 26.27 132 352 111 4 wt % of C 0.35 1.47 5.57 29.61 110 277 138 crosslinked E 0.32 1.39 5.22 27.82 86 120 264 PVOH Resin 4 with B 0.28 1.23 4.84 25.79 121 369 105 5 wt % of C 0.33 1.39 5.27 27.44 103 270 130 crosslinked E 0.32 1.34 5.08 26.96 83 136 247 PVOH

In Table 3, large changes in mechanical properties such as tensile impact strength and Charpy Impact are not observed for samples obtained from Resin 1. The other resins also had similar behavior in those mechanical properties (Table 3).

According to the results shown in Table 4, it can be observed that there was not a large change in melt index (MI) for HDPE modified with masterbatch samples using different methods B-E. Moreover, it is noted the amount of antioxidant (I-168 active Table 4) in the polymer after processing (either by extrusion or by blowmolding) depends on the method used to produce the samples, as expected. The samples obtained by method E have lower additive content but that did not damage the performance of the polymer properties, as showed in ESCR results (Table 2).

Post Consumer Resins (PCR)

The crosslinked polymeric additive (referred herein as MB) as formulated previously was added in post-consumer resins obtained from WISEWOOD COMPANY, BRAZIL, from small volume blown bottles of domestic trash. The crosslinking polymeric additive as described above was combined with PCR to final contents of 1, 3, 5 and 7 wt % of selectively crosslinked PVOH and processed in ZSK26 twin screw extruder or extrusion blow molding equipment. Table 5 presents the results of the mechanical tests and NPBI results obtained for the samples formulated with the post-consumer resins.

TABLE 5 IZOD impact ESCR (h) resistance at Flexural (ASTM D-1693 23° C. (J/m) Modulus (MPa) Sample procedure B) (ASTM D-256) (ASTM D-790) PBI N_(PBI) GF4950 from Braskem 32 112 1150 0.41 — Pure PCR 14 51.8 1203 0.09 1.00 PCR with 1 wt % of 32 52 1209 0.20 2.31 crosslinked PVOH PCR with 3 wt % of 34 50.2 1195 0.20 2.34 crosslinked PVOH PCR with 5 wt % of 53 54.2 1235 0.35 4.07 crosslinked PVOH PCR with 7 wt % of 92 58.2 1314 0.70 8.06 crosslinked PVOH

From the NPBI results, it is clear that the inventive composition increases the ESCR results maintaining and sometimes even increasing the impact resistance and flexural modulus of the base resin. The inventive polymer composition as described in the present disclosure is a reliable solution for the recycling of polymers, as normally those resins, due to the use and degradation suffered in the plastic production value chain, have a significant decrease in its ESCR, making it impossible to be used in noble applications that requires this property. It is also clear that even for compositions with very high PCR concentration (such as 99 wt %), the ESCR property achieved is similar to a virgin resin (GF4950). It is known by those skilled in the art that normally, to achieve such ESCR property, at least 30 wt % of virgin resin with very high ESCR need to be blended with PCR. The present invention enables the recycling of PCR in very high concentrations, being an environmental friendly solution for plastic waste.

Although the preceding description has been described herein with reference to particular means, materials and embodiments, it is not intended to be limited to the particulars disclosed herein; rather, it extends to all functionally equivalent structures, methods and uses, such as are within the scope of the appended claims. In the claims, means-plus-function clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents, but also equivalent structures. Thus, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface, in the environment of fastening wooden parts, a nail and a screw may be equivalent structures. It is the express intention of the applicant not to invoke 35 U.S.C. § 112(f) for any limitations of any of the claims herein, except for those in which the claim expressly uses the words ‘means for’ together with an associated function. 

1. A polymer composition comprising: a crosslinked polymeric additive composition comprising: a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent; and a secondary polymer composition.
 2. The polymer composition of claim 1, wherein the crosslinked polymeric additive composition is present at a percent by weight of the polymer composition that ranges from 0.5 wt % to 50 wt %.
 3. The polymer composition of claim 1, wherein the matrix polymer is present in a range of 30 wt % to 99.9 wt % of the crosslinked polymeric additive composition.
 4. The polymer composition of claim 1, wherein the one or more polymer particles is present in a range of 0.1 wt % to 70 wt % of the crosslinked polymeric additive composition.
 5. The polymer composition of claim 1, wherein the matrix polymer comprises one or more polymers selected from a group consisting of ethylene homopolymers, copolymers of ethylene and one or more C3-C20 alpha-olefins, propylene homopolymers, copolymers of propylene and one or more comonomers selected from ethylene or C4-C20 alpha-olefins, heterophasic propylene polymers, olefin terpolymers, and blends thereof.
 6. The polymer composition of claim 1, wherein the polar polymer comprises at least one functional group selected from the group consisting of hydroxyl, carboxylic acid, carboxylate, ester, ether, acetate, amide, amine, epoxy, imide, imine, sulfone, phosphone and their derivatives.
 7. The polymer composition of claim 1, wherein the polar polymer is selected from the group consisting of polyvinyl alcohol, ethylene vinyl alcohol copolymer, ethylene vinyl acetate copolymer and mixtures thereof.
 8. The polymer composition of claim 1, wherein the crosslinking agent is selected from the group consisting of maleic anhydride, maleic acid, itaconic acid, itaconic anhydride, succinic acid, succinic anhydride, succinic aldehyde, adipic acid, adipic anhydride, phthalic anhydride, pthalic acid, citric acid, glutaconic acid, glutaconic anhydride, glutaraldehyde, sodium tetraborate, organic titanates, organic zirconates, methoxy polyethylene glycol acrylates, ethoxy polyethylene glycol acrylates, ethylene glycol diacrylate, ethylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, 1,3-butylene glycol dimethacrylate, neopentyl glycol diacrylate, neopentyl glycol dimethacrylate, trimethylol ethane triacrylate, trimethylol ethane trimethacrylate, trimethylol propane triacrylate, trimethylol propane trimethacrylate, and tetramethylol methane tetracrylate, their derivatives and mixtures thereof.
 9. The polymer composition of claim 1, wherein the secondary polymer composition is one or more selected from a group consisting of polyolefin, polystyrene, polyamide, polyester, ethylene vinyl alcohol, polyacrylate, polymethacrylate, poly(vinyl chloride), polycarbonate, polyssacharides, and rubber.
 10. The polymer composition of claim 1, wherein the secondary polymer composition is one or more selected from a group consisting of polyethylene, polypropylene, polystyrene, poly(ethylene terephthalate), poly(vinyl chloride), polycarbonate, poly(methyl methacrylate) and nylon.
 11. The polymer composition of claim 1, wherein the secondary polymer composition is present in a range of 5 to 99 wt % of the polymer composition.
 12. The polymer composition of claim 1, wherein the polymer composition comprises one or more biobased polymers.
 13. The polymer composition of claim 1, wherein the polymer composition presents a Normalized Property Balance Index (N_(PBI)) greater than about 1.5, wherein the N_(PBI) is calculated according to the formula: ${N_{PBI} = \frac{P\; B\; I_{sample}}{P\; B\; I_{reference}}},$ where PBI_(sample) is the property balance index for a sample of the polymer composition, and PBI_(Reference) is the property balance index of a reference polymer composition consisting of the secondary polymer composition; and wherein PBI is calculated according to the formula: ${{P\; B\; I} = \frac{{FM} \times {IR} \times {ESCR}}{10^{7}}},$ where FM is the flexural modulus of the sample as determined by secant modulus of elasticity at 1% deformation according to ASTM D-790 in MPa, IR is the IZOD impact resistance according to ASTM D-256 in Jim, and ESCR is the environmental stress cracking resistance according to ASTM D-1693 procedure B in hours.
 14. The polymer composition of claim 1, wherein the polymer composition presents at least a 10% increase in environmental stress cracking resistance when compared to the environmental stress cracking resistance of the secondary polymer composition according to ASTM D-1693 procedure B.
 15. The polymer composition of claim 1, wherein the secondary polymer composition comprises a virgin polymer resin.
 16. The polymer composition of claim 1, wherein the secondary polymer composition comprises a post-industrial polymer resin, a post-consumer polymer resin, regrind polymer resin, or combinations thereof.
 17. The polymer composition of claim 15, wherein the secondary polymer is present in an amount higher than about 70 wt % of the polymer composition.
 18. A manufactured article comprising the polymer composition of claim
 1. 19. The manufactured article of claim 18, wherein the article is an injection molded article, a thermoformed article, a film, a foam, a blow molded article, a 3D printed article, a compressed article, a coextruded article, a laminated article, an injection blow molded article, a rotomolded article, an extruded article, or a pultruded article.
 20. A method, comprising: combining a crosslinked polymeric additive composition with a secondary polymer composition; wherein the crosslinked polymeric additive composition comprises a matrix polymer having a polar polymer internal phase that is selectively crosslinked with a crosslinking agent; and wherein combining the crosslinked polymeric additive composition with the secondary polymer compositions improves the environmental stress cracking resistance of the polymer composition with respect to the secondary polymer composition alone.
 21. The method of claim 20, wherein combining the crosslinked polymeric additive composition with a secondary polymer composition comprises a melt blend process.
 22. The method of claim 20, wherein combining the crosslinked polymeric additive composition with a secondary polymer composition comprises a dry blend process.
 23. The method of claim 20, wherein the secondary polymer composition comprises a post-industrial polymer resin, a post-consumer polymer resin, a regrind polymer resin, or combinations thereof.
 24. The method of claim 20, further comprising recycling the combined crosslinked polymeric additive composition with a secondary polymer composition.
 25. A polymer composition comprising: a masterbatch composition comprising: a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent; and a secondary polymer composition.
 26. A method comprising: combining a masterbatch composition with a secondary polymer composition, wherein the masterbatch composition comprises: a matrix polymer comprising a polyolefin, and one or more polymer particles dispersed in the polymer matrix, wherein the one or more polymer particles comprise a polar polymer selectively crosslinked with a crosslinking agent. 